Aim This study evaluated the influence of a wide diameter on extra-short dental implant stress distribution as a retainer for single implant-supported crowns in the atrophic mandible posterior region under axial and oblique load. Methods Four 3D digital casts of an atrophic mandible, with a single implant-retained crown with a 3:1 crown-to-implant ratio, were created for finite element analysis. The implant diameter used was either 4 mm (regular) or 6 mm (wide), both with 5 mm length. A 200 N axial or 30º oblique load was applied to the mandibular right first molar occlusal surface. The equivalent von Mises stress was recorded for the abutment and implant, minimum principal stress, and maximum shear stress for cortical and cancellous bone. Results Oblique load increased the stress in all components when compared to axial load. Wide diameter implants showed a decrease of von Mises stress around 40% in both load directions at the implant, and an increase of at least 3.6% at the abutment. Wide diameter implants exhibited better results for cancellous bone in both angulations. However, in the cortical bone, the minimum principal stress was at least 66% greater for wide than regular diameter implants, and the maximum shear stress was more than 100% greater. Conclusion Extra-short dental implants with wide diameter result in better biomechanical behavior for the implant, but the implications of a potential risk of overloading the cortical bone and bone loss over time, mainly under oblique load, should be investigated.

Abstract This study evaluated physicochemical properties of experimental infiltrants after addition of hydroxyapatite nanoparticles (HAp) or 58S bioactive glass (BAG) and diphenyliodonium hexafluorophosphate (DPI). The resin matrix was composed of TEGDMA/Bis-EMA (3:1), 0.5 mol% CQ, and 1 mol% EDAB. The blends received or not 0.5 mol% DPI and 10% wt BAG or HAp. Icon was used as commercial control. The groups were characterized by XRD, FT-IR spectrometry, and SEM before and after simulated body fluid (SBF) immersion for up to 7 days. Polymerization kinetics (n =3 ), water sorption and solubility (n=10), and viscosity (n = 3) were surveyed. For polymerization kinetics, the samples were polymerized for 5 min and the data were obtained from 40 s and 5 min. Statistical analysis was made using ANOVA and Tukey's test (a = 0.05). After 7 days of SBF immersion, XRD and FT-IR showed that the HAp crystalline phase was present only in the HAp groups. A lower degree of conversion (DC) and polymerization rate were observed for the Icon and BAG groups, whereas HAp showed higher values. For the BAG group, DPI increased polymerization rate and DC in 40 s. After 5 min, all groups presented DC above 80%. In groups with particles, the HAp groups exhibited higher viscosity, whereas DPI groups showed a decrease in viscosity. Icon had the highest water sorption. To conclude, BAG neither improved the physicochemical properties studied, nor did it show bioactive properties. The addition of DPI reduced viscosity caused by particle addition and also attenuated the DC decrease caused by BAG addition. The addition of bioactive particles to infiltrants should be seen with caution because they increase viscosity and may not bring major clinical improvements that justify their use. DPI might be indicated only if any component is added to the infiltrant to act as a compensation mechanism.

Abstract Zirconia-reinforced lithium silicate (ZLS) is a ceramic that promises to have better mechanical properties than other materials with the same indications as well as improved adaptation and fracture strength. Objective In this study, marginal and internal misfit and fracture load with and without thermal-mechanical aging (TMA) of monolithic ZLS and lithium disilicate (LDS) crowns were evaluated. Material and methods Crowns were milled using a computer-aided design/computer-aided manufacturing system. Marginal gaps (MGs), absolute marginal discrepancy (AMD), axial gaps, and occlusal gaps were measured by X-ray microtomography (n=8). For fracture load testing, crowns were cemented in a universal abutment, and divided into four groups: ZLS without TMA, ZLS with TMA, LDS without TMA, and LDS with TMA (n=10). TMA groups were subjected to 10,000 thermal cycles (5-55°C) and 1,000,000 mechanical cycles (200 N, 3.8 Hz). All groups were subjected to compressive strength testing in a universal testing machine at a crosshead speed of 1 mm/min until failure. Student’s t-test was used to examine misfit, two-way analysis of variance was used to analyze fracture load, and Pearson’s correlation coefficients for misfit and fracture load were calculated (α=0.05). The materials were analyzed according to Weibull distribution, with 95% confidence intervals. Results Average MG (p<0.001) and AMD (p=0.003) values were greater in ZLS than in LDS crowns. TMA did not affect the fracture load of either material. However, fracture loads of ZLS crowns were lower than those of LDS crowns (p<0.001). Fracture load was moderately correlated with MG (r=-0.553) and AMD (r=-0.497). ZLS with TMA was least reliable, according to Weibull probability. Conclusion Within the limitations of this study, ZLS crowns had lower fracture load values and greater marginal misfit than did LDS crowns, although these values were within acceptable limits.